Baja Karbon Tinggi Aksesoris las kawat inti Fluks
Aplikasi & Standar
1. Cocog kanggo welding baja karbon lan kekuatan sing cocog saka ketel, pipa, kendaraan,
bangunan, jembatan lan struktur liyane, kayata Q235.
2. Standar sing kita temui: GB/T5117 E4315, AWS, ISO2560-A:E 35 3 B 2 2, ISO 2560-B: E4315A
Isi karbon saka baja karbon dhuwur punika relatif dhuwur, weldability punika relatif miskin, welding kanggo preheat, sawise welding kanggo alon cooling utawa 350 derajat saka perawatan tempering suhu kurang, dawa tartamtu saka perawatan panas wis kekandelan workpiece kanggo nemtokake.
Komposisi kimia logam cair (%) Komposisi kimia C Mn Si SP Mo
Nilai dijamin &le~1,75 ≤0,60 &lele~0,45
Asil umum ≤0.10 ~ 1.40 ≤ 0.40&lele;0,025 ~ 0,30
Sifat mekanik Item uji Rm(MPa) ReL utawa Rp0,2(Mpa) A(%) KV2(J)
Nilai dijamin ≥590 ≥490 ≥15 ≥27 (-30 ℃)
Asil Umum 620 nganti 680 ≥500 20 nganti 28 ≥47
Isi hidrogen difusi logam cair: ≤4.0ml/100g(metode Gliserol)
Deteksi cacat sinar-X: kelas Ⅰ
Arus referensi (AC, DC+) diameter elektroda (mm) φ3.2φ4.0φ5.0
Arus las (A) 80~140 110~210 160~230
Fitur
1. Low sodium elektroda hidrogen karo busur stabil, wangun apik banget, cipratan cilik, lan ripple kepileh.
2. Karakteristik mekanik sing konsisten, plastisitas sing kuat, tahan impact, lan tahan retak.
Produk utama kita yaiku paduan kromium-molibdenum, paduan tahan panas, paduan berbasis nikel, paduan dupleks lan super duplex.Kalebu elektroda busur manual, MIG / MAG, TIG, kabel busur submerged lan macem-macem kabel flux-cored.Produk kasebut akeh digunakake ing welding baja paduan rendah, baja tahan panas, campuran dasar nikel lan macem-macem baja tahan karat kanthi kekuatan dhuwur lan kateguhan suhu rendah.
Perusahaan & Pabrik
Komposisi produk lan sifat mekanik introduksi
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| ATURAN GB/T | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | - | - | ≥0.10 |
| ATURAN AWS | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | 0.030 | 0.030 | ≥0.10 |
| NILAI CONTOH | 0,068 | 1.28 | 0.28 | 0.03 | 1.65 | 0.42 | 0.011 | 0.007 | 0.01 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | HEATTREAMENT ℃ xh | NILAI IMPAK J/℃ | ELONGASI(%) | |||||||||
| ATURAN GB/T | 490 | 590 | 620*1 | 27/-20 | 16 | |||||||||
| ATURAN AWS | 530 | 620 | 620*1 | - | 17 | |||||||||
| NILAI CONTOH | 600 | 685 | 620*1 | 80/-50 | 25 | |||||||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||||
| LISTRIK (Amp) | H/W | 80-110 | 100-130 | 130-180 | 180-230 | |||||
| OW | 50-80 | 90-120 | 130-160 | - | ||||||
CATETAN:
H/W: pengelasan posisi horizontal
O/W: welding posisi over-head
KASUS KHAS
Sertifikat
Komposisi produk lan sifat mekanik introduksi:
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| ATURAN GB/T | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | - | - | ≥0.10 |
| ATURAN AWS | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | 0.030 | 0.030 | ≥0.10 |
| NILAI CONTOH | 0,068 | 1.28 | 0.28 | 0.03 | 1.65 | 0.42 | 0.011 | 0.007 | 0.01 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | HEATTREAMENT ℃ xh | NILAI IMPAK J/℃ | ELONGASI(%) | |||||||||
| ATURAN GB/T | 490 | 590 | 620*1 | 27/-20 | 16 | |||||||||
| ATURAN AWS | 530 | 620 | 620*1 | - | 17 | |||||||||
| NILAI CONTOH | 600 | 685 | 620*1 | 80/-50 | 25 | |||||||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||||
| LISTRIK (Amp) | H/W | 80-110 | 100-130 | 130-180 | 180-230 | |||||
| OW | 50-80 | 90-120 | 130-160 | - | ||||||
CATETAN:
H/W: pengelasan posisi horizontal
O/W: welding posisi over-head