Elektroda Tangan 430Mpa Kanggo Baja Karbon Rendah
Aplikasi & Standar & Cathetan:
1. Welding kekuatan biasa saka struktur baja karbon kurang lan bahan kekuatan kurang saka baja alloy kurang.
2. Standar sing kita temoni: GB/T5117 E4303, AWS, ISO2560-A:E 35 0 R 1 2, ISO 2560-B: E4303A, JIS Z3211 E4303
1. Insulator kudu dimasak, lan elektroda kudu dipanggang ing 180 ° C. Nalika lagi dilas ing bengkel, kudu diselehake ing silinder insulasi.
2. Pay care nalika welding: Kanggo mesthekake wilayah welding resik, iku penting kanggo mbusak sembarang lenga utawa rereged liyane saka radius 20mm watara welding sadurunge welding. Welds kudu resik, padhang, lan ora karat. Wangun welding sing tepat dibutuhake (miturut welding welding manual welding) 3. Lingkungan welding, kalebu angin lan bledug. Pay manungsa waé, 4, tingkat welding: dawa welding rod welding khas 40CM.
Fitur
1. Titanium kalsium tipe c hemisal kulit karbon baja elektroda.
2. Stabil busur, slag fluidity apik, aman slag gampang, cipratan cilik, wangun ayu.
Jeneng Cina kanggo elektroda tangan karbon rendah GEM-F03 yaiku J422, dene label internasional yaiku E4303. J stands for elektroda baja struktural, 42 padha karo 420 kg/mm2, lan nuduhake kekuatan tensile saka logam weld. Iki minangka elektroda asam saka jinis kalsium titanium sing dilapisi. Digunakake kanggo welding struktur baja karbon LOW lan gelar kekuatan kurang saka baja alloy kurang, umume digunakake kanggo welding struktur baja lan pipa baja karbon standar.
Perusahaan & Pabrik
Komposisi produk lan sifat mekanik introduksi
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| ATURAN GB/T | 0.2 | 1.2 | 1 | 0.2 | 0.3 | 0.3 | 0.04 | 0.035 | 0.08 |
| ATURAN AWS | - | - | - | - | - | - | - | - | - |
| NILAI CONTOH | 0,076 | 0.5 | 0.38 | 0,025 | 0.01 | 0,028 | 0.016 | 0.01 | 0.008 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | HEATTREAMENT ℃ xh | ||||||
| ATURAN GB/T | 330 | 430 | AW | ||||||
| ATURAN AWS | - | - | AW | ||||||
| NILAI CONTOH | 468 | 538 | AW | ||||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
| LISTRIK | H/W | 80-120 | 90-140 | 150-190 | 180-240 | ||||
| (Amp) | O/W | 50-80 | 90-120 | 130-160 | - | ||||
CATETAN:
H/W: pengelasan posisi horizontal
O/W: welding posisi over-head
Kasus Khas
Sertifikat
Komposisi produk lan sifat mekanik introduksi
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| ATURAN GB/T | 0.2 | 1.2 | 1 | 0.2 | 0.3 | 0.3 | 0.04 | 0.035 | 0.08 |
| ATURAN AWS | - | - | - | - | - | - | - | - | - |
| NILAI CONTOH | 0,076 | 0.5 | 0.38 | 0,025 | 0.01 | 0,028 | 0.016 | 0.01 | 0.008 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | HEATTREAMENT ℃ xh | ||||||
| ATURAN GB/T | 330 | 430 | AW | ||||||
| ATURAN AWS | - | - | AW | ||||||
| NILAI CONTOH | 468 | 538 | AW | ||||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
| LISTRIK | H/W | 80-120 | 90-140 | 150-190 | 180-240 | ||||
| (Amp) | O/W | 50-80 | 90-120 | 130-160 | - | ||||
CATETAN:
H/W: pengelasan posisi horizontal
O/W: welding posisi over-head