Stainless Steels Flux Cored Wire R316LT1-5 Bahan las aluminium
TEKNOLOGI WELDING
Aja nganti pitakonan
Terus ngganggu sampeyan
Ketidakstabilan Arc
Molding sing ora apik
Kakehan spatter
Iku cocok kanggo welding 18% Cr-12% Ni-2% Mo stainless steel (SUS316L, etc.) ing industri petrokimia, prau meksa, tank panyimpenan suhu kurang, pupuk, urea, mesin pangan lan industri liyane.
Komponen utama yaiku karbon rendah 18% Cr-12% Ni-2% Mo
Ripple apik
Mburi tanpa Isi munggah, sampeyan bisa njaluk dalan las banget
Wangun saka weld pass ayu, aman slag gampang, lan proses welding wis kinerja banget.
Gampang slagging
Parameter produk
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
| ATURAN GB/T | 0,023 | 0.6 | 1.40 | 0,025 | 0.002 | 11.6 | 18.9 | 2.8 | - |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
| ATURAN GB/T | - | 654 | 35 | - | - | |||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | Ketebalan plating (mm) | Bukaan akar (mm) | Listrik (Amp) | |||||
| 2.2*915 | 2~4 | 2.0 | 80-100 | |||||
| 5~9 | 2.5 | 90-120 | ||||||
| ≥10 | 3.0 | 90-130 | ||||||
Dhukungan pabrik
Produk kasebut cocog kanggo a
sawetara saka sudhut aplikasi
TEKNOLOGI WELDING
-
Mei Jin Hua Sheng
menara sintetik glikol
-
300.000-ton Ngambang
Produksi Storage Tanker (FPSO)
Guangxi Huayi
menara dehidrasi metanol
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
| ATURAN GB/T | 0,023 | 0.6 | 1.40 | 0,025 | 0.002 | 11.6 | 18.9 | 2.8 | - |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
| ATURAN GB/T | - | 654 | 35 | - | - | |||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | Ketebalan plating (mm) | Bukaan akar (mm) | Listrik (Amp) | |||||
| 2.2*915 | 2~4 | 2.0 | 80-100 | |||||
| 5~9 | 2.5 | 90-120 | ||||||
| ≥10 | 3.0 | 90-130 | ||||||