Stainless Steels Flux Cored Wire R347T1-5 Bahan las wadah
TEKNOLOGI WELDING
Aja nganti pitakonan
Terus ngganggu sampeyan
Ketidakstabilan Arc
Molding sing ora apik
Kakehan spatter
Komponen utama yaiku karbon rendah 18% Cr-8% Ni-Nb
Iku cocok kanggo soldering saka 18% Cr-8% Ni-Nb stainless steel (SUS347) lan 18% Cr-8% Ni-Ti
sambungan pipa baja tahan karat (SUS321) ing industri petrokimia, bejana tekanan,
tank panyimpenan suhu kurang, pupuk, urea, mesin pangan lan industri liyane.
Ripple apik
Korosi intergranular sing apik banget
resistensi amarga tambahan Nb
Mburi tanpa Isi munggah, sampeyan bisa njaluk dalan las banget; Bentuk weld pass
iku ayu, aman slag gampang, lan proses welding wis kinerja banget.
Gampang slagging
Parameter produk
KOMPONEN KIMIA:
ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
ATURAN GB/T | 0.02 | 0.6 | 1.70 | 0.02 | 0.002 | 9.7 | 18.3 | 0.01 | Nb:0.63 |
PROPERTI MEKANIKAL:
PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | - | 720 | 35 | - | - |
PARAMETER WELDING REKOMENDASI:
SPESIFIKASI DIAMETER (mm) | Ketebalan plating (mm) | Bukaan akar (mm) | Listrik (Amp) | |||||
2.2*915 | 2~4 | 2.0 | 80-100 | |||||
5~9 | 2.5 | 90-120 | ||||||
≥10 | 3.0 | 90-130 |
Dhukungan pabrik
Produk kasebut cocog kanggo a
sawetara saka sudhut aplikasi
TEKNOLOGI WELDING
-
Tangki panyimpenan Shanghai Morimatsu
-
10000TEU kapal kontainer
-
Proyek YAMAL LNG
KOMPONEN KIMIA:
ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
ATURAN GB/T | 0.02 | 0.6 | 1.70 | 0.02 | 0.002 | 9.7 | 18.3 | 0.01 | Nb:0.63 |
PROPERTI MEKANIKAL:
PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | - | 720 | 35 | - | - |
PARAMETER WELDING REKOMENDASI:
SPESIFIKASI DIAMETER (mm) | Ketebalan plating (mm) | Bukaan akar (mm) | Listrik (Amp) | |||||
2.2*915 | 2~4 | 2.0 | 80-100 | |||||
5~9 | 2.5 | 90-120 | ||||||
≥10 | 3.0 | 90-130 |