Stainless Steels Flux Cored Wire R309LT1-5 LNG kendaraan botol bahan las
TEKNOLOGI WELDING
Aja nganti pitakonan
Terus ngganggu sampeyan
Ketidakstabilan Arc
Molding sing ora apik
Kakehan spatter
Cocog kanggo baja tahan karat lan baja karbon utawa welding baja sing beda karo baja paduan rendah, pipa baja karbon welding lan pipa baja stainless austenitik welding ngisor.
Komponen utama yaiku karbon rendah 22% Cr-12% Ni
Ripple apik
Mburi tanpa Isi munggah, sampeyan bisa njaluk dalan las banget
Wangun weld pass ayu, aman slag gampang, lan proses welding wis kinerja banget
Gampang slagging
Parameter produk
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
| ATURAN GB/T | 0.015 | 0.45 | 1.30 | 0.015 | 0.001 | 12.9 | 24.4 | 0.02 | - |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
| ATURAN GB/T | - | 650 | 36 | - | - | |||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | Ketebalan plating (mm) | Bukaan akar (mm) | Listrik (Amp) | |||||
| 2.2*915 | 2~4 | 2.0 | 80-100 | |||||
| 5~9 | 2.5 | 90-120 | ||||||
| ≥10 | 3.0 | 90-130 | ||||||
Dhukungan pabrik
Produk kasebut cocog kanggo a
sawetara saka sudhut aplikasi
TEKNOLOGI WELDING
-
Bahan welding kanggo wesi aluminium
-
Telung lawang 2 # ora aktif
-
300.000-ton operator akeh
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
| ATURAN GB/T | 0.015 | 0.45 | 1.30 | 0.015 | 0.001 | 12.9 | 24.4 | 0.02 | - |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
| ATURAN GB/T | - | 650 | 36 | - | - | |||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | Ketebalan plating (mm) | Bukaan akar (mm) | Listrik (Amp) | |||||
| 2.2*915 | 2~4 | 2.0 | 80-100 | |||||
| 5~9 | 2.5 | 90-120 | ||||||
| ≥10 | 3.0 | 90-130 | ||||||
Tulis pesen sampeyan ing kene lan kirimake menyang kita