Kawat Cored Fluks Baja Tahan Karat E347T1-1/4 LNG exp ort pipeline project weld
TEKNOLOGI WELDING
Aja nganti pitakonan
Terus ngganggu sampeyan
Ketidakstabilan Arc
Molding sing ora apik
Kakehan spatter
Resistance karat intergranular banget amarga saka
tambahan Nb; Kabeh welding posisi, welding pass Gamelan
Busur iku alus lan stabil, kurang cipratan, mbentuk ayu, slag apik
njabut, kabel stabil dipakani, karo kinerja proses welding banget.
Ripple apik
Tipe kalsium titanium
elektroda tangan stainless steel
Komponen utama yaiku 1 8% Cr- 9% Ni
Gampang slagging
Parameter produk
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
| ATURAN GB/T | 0.02 | 0.65 | 1.40 | 0.018 | 0.003 | 9.4 | 20.2 | 0.015 | Nb:0,5 Cu:0,01 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
| ATURAN GB/T | - | 665 | 40 | - | - | |||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 1.2 | 1.6 | |||
| Tegangan (Volt) | 20-36 | 24-38 | |||
| Listrik (Amp) | 120-260 | 200-300 | |||
| Kacepetan (mm/min) | 15-25 | 18-25 | |||
| dawa regangan garing (mm) | 15-25 | 15-25 |
Dhukungan pabrik
Produk kasebut cocog kanggo a
sawetara saka sudhut aplikasi
TEKNOLOGI WELDING
-
Bahan welding kanggo wesi aluminium
-
9.000 ton bahan kimia
-
China-rusia sisih wétan
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Liyane |
| ATURAN GB/T | 0.02 | 0.65 | 1.40 | 0.018 | 0.003 | 9.4 | 20.2 | 0.015 | Nb:0,5 Cu:0,01 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongation/% | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
| ATURAN GB/T | - | 665 | 40 | - | - | |||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 1.2 | 1.6 | |||
| Tegangan (Volt) | 20-36 | 24-38 | |||
| Listrik (Amp) | 120-260 | 200-300 | |||
| Kacepetan (mm/min) | 15-25 | 18-25 | |||
| dawa regangan garing (mm) | 15-25 | 15-25 |