Paduan nikel MIG ERNiCr-3 Sambungan solder
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| ATURAN GB/T | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67 | - | 3.0 | 2.0-3.0 | - | - |
| ATURAN AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67 | - | 3.0 | 2.0-3.0 | 0.03 | 0.02 |
| NILAI CONTOH | 0,023 | 2.81 | 0.09 | 20.15 | 72.86 | 0.19 | 0.84 | 2.46 | 0.001 | 0.004 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | NILAI IMPAK J/℃ | ELONGASI(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | 550 | - | - | ||||
| NILAI CONTOH | - | 675 | 92/-196 | 42 | ||||
Komposisi utama yaiku 72Ni-20Cr-3Mn-2.5Nb + Ta, kawat las argon paduan nikel-kromium.
Logam molten nduweni sifat mekanik sing apik lan tahan kanggo korosi pitting lan korosi celah.
Pakan kabel Gamelan, busur stabil, mbentuk ayu, aliran apik saka wesi molten, kurang cipratan, karo kinerja proses welding banget.
-
85000 m3 Pembawa Etilena Etana Gedhe Banget (VLEC)
-
Proyek LNG Kanada
Harbin listrik telung lawang CMT
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| ATURAN GB/T | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67 | - | 3.0 | 2.0-3.0 | - | - |
| ATURAN AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67 | - | 3.0 | 2.0-3.0 | 0.03 | 0.02 |
| NILAI CONTOH | 0,023 | 2.81 | 0.09 | 20.15 | 72.86 | 0.19 | 0.84 | 2.46 | 0.001 | 0.004 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | NILAI IMPAK J/℃ | ELONGASI(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | 550 | - | - | ||||
| NILAI CONTOH | - | 675 | 92/-196 | 42 | ||||