Paduan nikel Elektroda manual pembuatan las ENi-1
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| ATURAN GB/T | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| ATURAN AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| NILAI CONTOH | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | NILAI IMPAK J/℃ | ELONGASI(%) | ||||
| ATURAN GB/T | 200 | 410 | - | 18 | ||||
| ATURAN AWS | - | 410 | - | 20 | ||||
| NILAI CONTOH | 310 | 435 | - | 29 | ||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| LISTRIK (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Elektroda tangan titanium-kalsium, komposisi nominal (persen bobot) yaiku 95Ni-2.5Ti.
Stabil busur, ayu mbentuk, sethitik cipratan, aman slag gampang, resistance porosity apik.
Logam sing digabung nduweni sifat mekanik sing apik, tahan panas, tahan korosi, fusi lan tahan retak.
Bahan welding seri baja Cr-Mo lan bahan welding permukaan elektroda digunakake kanthi akeh ing peralatan panyulingan petroleum
-
158.000 ton kapal tanker Suez
Supercore SG
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| ATURAN GB/T | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| ATURAN AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| NILAI CONTOH | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
PROPERTI MEKANIKAL:
| PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | NILAI IMPAK J/℃ | ELONGASI(%) | ||||
| ATURAN GB/T | 200 | 410 | - | 18 | ||||
| ATURAN AWS | - | 410 | - | 20 | ||||
| NILAI CONTOH | 310 | 435 | - | 29 | ||||
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| LISTRIK (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||