Low-Alloy Steels Manual Elektroda E7016-C2L komponen Reaktor welding
Komposisi utama yaiku baja 3,5% Ni, rod welding tangan jinis kalium hidrogen rendah, ing suhu operasi -75C, leleh.
Ketangguhan impact saka logam apik banget.
Busur stabil, kurang cipratan, cetakan apik, gampang mbusak slag, kinerja X-Rav apik banget.
KOMPONEN KIMIA:
ALLOY (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Liyane | |
ATURAN GB/T | 0.038 | 0.19 | 0.64 | 0.006 | 0.004 | 3.56 | 0.033 | 0.8 | - |
PROPERTI MEKANIKAL:
PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongasi (%) | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | 475 | 550 | 28 | 65/-100 | 620*1 |
PARAMETER WELDING REKOMENDASI:
SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
LISTRIK (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |
Reaktor internal
-
Lapangan minyak Qinghai Youjian Wunan
-
308.000 ton kapal minyak mentah VLCC
KOMPONEN KIMIA:
ALLOY (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Liyane | |
ATURAN GB/T | 0.038 | 0.19 | 0.64 | 0.006 | 0.004 | 3.56 | 0.033 | 0.8 | - |
PROPERTI MEKANIKAL:
PROPERTI | KEKUATAN PENGHASILAN (MPa) | KEKUATAN EXTENSION (MPa) | Elongasi (%) | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | 475 | 550 | 28 | 65/-100 | 620*1 |
PARAMETER WELDING REKOMENDASI:
SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
LISTRIK (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |