Hard-madhep Elektroda Manual EDCrNi-B-15 sambungan fabrikasi las
Stabilitas arc
wangun ayu
Splash banget sethitik
Gampang slagging
Resistance stotal apik
Wong sing stabil
Aplikasi
Utamane digunakake kanggo lumahing permukaan sealing katup tekanan dhuwur sing suhu kerja ing ngisor 600 ℃.
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | Nb | P | S | |
| ATURAN GB/T | 0.18 | 0.60-5.00 | 3.80-6.50 | 14.00-21.00 | 6.50-12.00 | 3.50-7.00 | 0.50-1.20 | 0.04 | 0.03 | |
| ATURAN AWS | - | - | - | - | - | - | - | - | - | |
| NILAI CONTOH | 0.05 | 1.26 | 5.34 | 16.1 | 8.1 | 3.8 | 0.61 | 0,028 | 0.007 | |
Kekerasan WELD PASS:
Nilai conto HRC=40
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 3.2*350 | 4.0*350 | 5.0*350 | ||||||||
| LISTRIK (Amp) | 80-120 | 120-160 | 160-210 | ||||||||
Low-sodium hidrogen tamba lapisan Cr-Ni-Si-Mo klep lumahing elektroda;
Logam lumahing minangka jumlah cilik saka struktur austenite ferrite, wis resistance suhu dhuwur apik, resistance erosi lan sifat liyane, atose suhu dhuwur, stabilitas termal apik lan resistance lemes termal.
Kanthi nambah wektu tuwa, kekerasan lan resistensi abrasi saka permukaan logam luwih apik.
Ningbo Chengwei Metal Material Co., Ltd. minangka perusahaan profesional welding internasional kanthi riset lan pangembangan, produksi, penjualan lan manajemen. Iki diadegaké ing 2020.
10 set kaleng bola 4000m³ saka Nanjing Jinling Petrochemical
Nanjing Chengzhi Yongqing Energy 07MnNiMoDR steel ethylene ball tank
Zhejiang Petrokimia diesel/tangki penyimpanan minyak mentah
KOMPONEN KIMIA:
| ALLOY (wt%) | C | Mn | Si | Cr | Ni | Mo | Nb | P | S | |
| ATURAN GB/T | 0.18 | 0.60-5.00 | 3.80-6.50 | 14.00-21.00 | 6.50-12.00 | 3.50-7.00 | 0.50-1.20 | 0.04 | 0.03 | |
| ATURAN AWS | - | - | - | - | - | - | - | - | - | |
| NILAI CONTOH | 0.05 | 1.26 | 5.34 | 16.1 | 8.1 | 3.8 | 0.61 | 0,028 | 0.007 | |
WELD PASS atose
Nilai conto HRC=40
PARAMETER WELDING REKOMENDASI:
| SPESIFIKASI DIAMETER (mm) | 3.2*350 | 4.0*350 | 5.0*350 | ||||||||
| LISTRIK (Amp) | 80-120 | 120-160 | 160-210 | ||||||||